Mn13 High Manganese Steel Plate
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match.
- Overview
- Related Products
Description:
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match. Under the action of large impact load or large contact stress, the surface of the steel plate is work hardened, and the surface hardness is rapidly increased from HB200 to above HB500, thereby producing a highly wear-resistant surface layer, while the inner austenite of the steel plate still maintains good impact toughness.
There are two characteristics of high manganese steel:
1.The greater the external impact load, the higher the wear resistance of its own surface layer;
2.As the surface hardened layer gradually wears away, a new work hardening layer will be continuously formed.
The special properties of high manganese steel are suitable for making wear-resistant components that withstand long-term wear of high impact materials. It has long been widely used in mechanical equipment such as metallurgy, mining, building materials, railways, electricity, and coal.
Specifications:
|
Item |
MN13 |
|
Width |
1000 up to 3000mm |
|
Standard Grade |
DIN:1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 EN : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF : FORA500, FORA400,; Creusabro8000, Creusabro4800 GB : NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS : JFE-EH400, JFE-EH360, JFE-EH500; WEL-HARD500, WEL-HARD400 |
|
Technological process |
controlled rolling, hot-rolled, normalizing, tempering, annealing, quenching, N+T, Q+T |
|
Thickness |
2 up to 300mm |
|
Surface |
clean, blasting, finishing, and painting |
|
Length |
1000 up to 12000mm |
Equivalent Grades of Mn13:
|
GB |
EN |
ASTM |
AFNOR |
|
Mn13 |
1.3401-X120Mn13 |
A128GrB2 |
X120Mn13 |
Mn13 Chemical Composition:
|
Grade |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90~1.20 |
0.3~0.8 |
11.0~14.0 |
≤0.035 |
≤0.030 |
Mn13 Mechanical Property:
|
Grade |
Tensile Strength(Mpa) |
Elongation (%) |
Impact Performance(20℃) |
Initial Hardness Value (HB) |
Hardness Value After Hardening (HB) |
Cold Bending(180°) |
|
Mn13 |
≥800 |
≥40 |
ak≥90（J） |
200-250 |
>300 |
Qualified |
Applications:
Mn13 is often used to make shovel teeth of excavators, rolling wall and crushing wall of cone crushers, fork plates of jaw crushers, lining plates of ball mills, railway switches, plate hammers, hammer heads, etc.
Product Packing:
We uses the most safest and the most effective ways of packaging for all types of deliveries.
FAQ:
1.Q: How long can make delivery?
A: For stock products, will make shipments in 5- 7 days after receiving deposit; for products need new production for common materials, usually make shipments in 10-15 days; for products need new production for special and rare materials, usually need 20-30 days to make shipment.
2.Q:Can I visit your factory?
A: Sure,welcome to you visit our factory at any time.
3.Q:Where are you?
A: Anyang in Henan Province.
4.Q: What certifications do your products have?
A: We have ISO 9001,BV, SGS, CE, TUV and other certifications.
5.Q:What are your terms of payment?
A:30% T/T deposit in advance, 70% T/T balance within 5 days after B/L copy, 100%.Irrevocable L/C at sight, 100% Irrevocable L/C after receive B/L 30-120 days, O/A.
Tag:
Mn13, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel