X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- 概要
- 関連製品
説明:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
ボーマン steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
仕様：
|
商品名 |
High Manganese steel plate |
|
材料 |
Din 1.3401, K700, Mn13, X120Mn12 |
|
ブランド |
TISCO, Bao Steel |
|
スタンダード |
DIN, GB, ISO, JIS, AISI, ASTM |
|
長さ |
2mへ7m |
|
幅（Width） |
1mへ2m |
|
厚さ |
3mmへ50mm |
同等グレード 120Mn12 の:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25-0.50 |
≤0.100 |
≤0.040 |
1.50 |
120Mn12 の Mechanical Properties at Room Temperature:
|
学年 |
抗張力 |
降伏強さ |
伸長 |
Shock Absorption (Water) |
硬度 |
|
120Mn12 の |
880〜1130 MPa |
≧410MPa |
≥40％ |
124 J (at room temperature) |
≤ 229HB |
機能と特徴：
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
アプリケーション：
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
製品パッキング：
当社では、あらゆるタイプの配送に対して、最も安全かつ効果的な梱包方法を採用しています。
FAQ：
1.Q: 配達にはどのくらい時間がかかりますか?
A: 在庫品の場合、入金受領後 5 ～ 7 日以内に発送します。一般的な材料の新規生産が必要な製品の場合、通常 10 ～ 15 日以内に発送します。特殊および希少材料の新規生産が必要な製品の場合、通常 20 ～ 30 日で発送します。
2.Q: あなたの工場を訪問できますか?
A: はい、いつでも当社の工場を訪問することを歓迎します。
3.Q:どこにいますか?
A: 河南省の安陽です。
4.Q: あなたの製品にはどのような認証がありますか?
A: ISO 9001、BV、SGS、CE、TUV、その他の認証を取得しています。
5.Q: 支払い条件は何ですか?
A: 事前に 30% T/T デポジット、B/L コピー後 70 日以内に 5% T/T 残高、一覧払い 100% 取消不能 L/C、B/L 受領後 100-30 日以内に 120% 取消不能 L/C、O/A。
タグ：
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 高マンガン鋼板