Q235C Carbon Steel Pipe
Q235C carbon steel pipe belongs to the higher quality grade material in the Q235 series. Compared with Q235A and Q235B, its core advantage lies in stricter chemical composition control and better low-temperature impact toughness.
"Q" in the grade represents yield strength, "235" means that the lower limit of yield strength is 235MPa, and "C" indicates that its quality grade is C grade, which must meet the impact toughness requirements under 0℃ conditions, significantly improving the service safety of the material in low temperature environments.
- 概要
- 関連製品
説明:
Q235C carbon steel pipe belongs to the higher quality grade material in the Q235 series. Compared with Q235A and Q235B, its core advantage lies in stricter chemical composition control and better low-temperature impact toughness. "Q" in the grade represents yield strength, "235" means that the lower limit of yield strength is 235MPa, and "C" indicates that its quality grade is C grade, which must meet the impact toughness requirements under 0℃ conditions, significantly improving the service safety of the material in low temperature environments.
Q235C has stronger environmental adaptability. Its welding performance is better than that of grade A and B steels. It can be welded by submerged arc welding, gas shielded welding and other processes. The preheating temperature before welding is relatively low, and the embrittlement tendency of the heat affected zone after welding is small. It is often used in key welding parts such as pressure vessel shells and port machinery components. In terms of cold processing performance, the material can be formed by cold bending, stamping and other processes. The 180° cold bending test with a bending core diameter equal to the thickness of the specimen is qualified, meeting the manufacturing needs of complex structural parts. According to the standard, the lower limit of Q235C's working temperature can reach -20℃ (specific requirements need to be combined with design specifications), and it is widely used in outdoor steel structures, refrigeration equipment brackets and other fields in cold northern regions.
According to national standards, Q235C is usually supplied in a hot-rolled state, and iron oxide is allowed to exist on the surface. It can also be sandblasted or pickled according to demand. In addition to conventional tensile and bending tests, quality inspection must perform a 0℃ impact test, and ultrasonic flaw detection or magnetic particle testing must be performed to ensure that there are no major defects inside the material. Compared with Q235B, its production cost increases by about 8%-12%, but it still has an economic advantage compared to Q235D steel that requires -20℃ impact performance guarantee.
仕様：
|
商品名 |
Q235C Carbon Steel Pipe |
|
スタンダード |
AISI ASTM JIS BS DIN GB |
|
技術 |
つや出し |
|
厚さ |
0.5〜40 mm |
|
OD |
15-300mm |
|
長さ |
5.8-12M |
|
サンプル |
自由にサンプル |
|
梱包 |
標準的な耐航梱包または必要に応じて |
|
お支払について |
T/T、L/C、 |
Q235C Carbon Steel Pipe Chemical Composition:
|
学年 |
C％ |
Si％ |
Mn％ |
P％ |
S％ |
|
Q235C |
≤0.17 |
≤0.35 |
≤1.4 |
≤0.040 |
≤0.040 |
Q235C Carbon Steel Mechanical Property:
|
厚さ |
降伏強さ（Mpa） |
抗張力 |
伸長 |
衝撃エネルギー |
|
|
（MM） |
（MPa） |
（％） |
最小値 |
||
|
≤16 |
235 |
370-500 |
26 |
0 |
27J |
|
> 16-40 |
225 |
370-500 |
25 |
0 |
27J |
|
> 40 |
215 |
370-500 |
24 |
0 |
27J |
|
最小衝撃エネルギーは縦方向エネルギーである |
|||||
製品パッキング：
Standard packing or according to customer requirements.
FAQ：
1.Q: 配達にはどのくらい時間がかかりますか?
A: 在庫品の場合、入金受領後 5 ～ 7 日以内に発送します。一般的な材料の新規生産が必要な製品の場合、通常 10 ～ 15 日以内に発送します。特殊および希少材料の新規生産が必要な製品の場合、通常 20 ～ 30 日で発送します。
2.Q: あなたの工場を訪問できますか?
A: はい、いつでも当社の工場を訪問することを歓迎します。
3.Q:どこにいますか?
A: 河南省の安陽です。
4.Q: あなたの製品にはどのような認証がありますか?
A: ISO 9001、BV、SGS、CE、TUV、その他の認証を取得しています。
5.Q: 支払い条件は何ですか?
A: 事前に 30% T/T デポジット、B/L コピー後 70 日以内に 5% T/T 残高、一覧払い 100% 取消不能 L/C、B/L 受領後 100-30 日以内に 120% 取消不能 L/C、O/A。
タグ：
Q235C Carbon Steel Pipe, China Carbon Steel PipeManufacturers, Suppliers, Factory, Carbon Steel, Carbon steel Tube,Carbon Steel Pipe,Q235 炭素鋼管,Q235A 炭素鋼管,Q235B 炭素鋼管