Mn13 čelična ploča s visokim sadržajem mangana
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match.
- SAŽETAK
- Srodni proizvodi
Opis:
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match. Under the action of large impact load or large contact stress, the surface of the steel plate is work hardened, and the surface hardness is rapidly increased from HB200 to above HB500, thereby producing a highly wear-resistant surface layer, while the inner austenite of the steel plate still maintains good impact toughness.
There are two characteristics of high manganese steel:
1.The greater the external impact load, the higher the wear resistance of its own surface layer;
2.As the surface hardened layer gradually wears away, a new work hardening layer will be continuously formed.
The special properties of high manganese steel are suitable for making wear-resistant components that withstand long-term wear of high impact materials. It has long been widely used in mechanical equipment such as metallurgy, mining, building materials, railways, electricity, and coal.
Tehnički podaci:
|
Stavka |
MN13 |
|
Širina |
1000 do 3000 mm |
|
Standardni stupanj |
DIN:1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 HR : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF : FORA500, FORA400,; Creusabro8000, Creusabro4800 GB: NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS: JFE-EH400, JFE-EH360, JFE-EH500; WEL-HARD500, WEL-HARD400 |
|
Tehnološki postupak |
kontrolirano valjanje, toplo valjano, normalizacija, kaljenje, žarenje, kaljenje, N+T, Q+T |
|
Debljina |
2 do 300 mm |
|
Površinski |
čišćenje, pjeskarenje, završna obrada i bojanje |
|
Dužina |
1000 do 12000 mm |
Equivalent Grades of Mn13:
|
GB |
EN |
ASTM |
AFNOR |
|
Mn13 |
1.3401-X120Mn13 |
A128GrB2 |
X120Mn13 |
Mn13 Chemical Composition:
|
Razred |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90 ~ 1.20 |
0.3 ~ 0.8 |
11.0 ~ 14.0 |
≤ 0.035 |
≤ 0.030 |
Mn13 Mechanical Property:
|
Razred |
Vlačna čvrstoća (Mpa) |
Istezanje (%) |
Impact Performance(20℃) |
Initial Hardness Value (HB) |
Hardness Value After Hardening (HB) |
Cold Bending(180°) |
|
Mn13 |
≥ 800 |
≥ 40 |
ak≥90（J） |
200-250 |
> 300 |
Kvalificiran |
Primjena:
Mn13 is often used to make shovel teeth of excavators, rolling wall and crushing wall of cone crushers, fork plates of jaw crushers, lining plates of ball mills, railway switches, plate hammers, hammer heads, etc.
Pakiranje proizvoda:
Za sve vrste dostava koristimo najsigurnije i najučinkovitije načine pakiranja.
PITANJA:
1.P: Koliko dugo može biti isporuka?
O: Za proizvode na zalihama isporučujemo u roku od 5-7 dana nakon primitka pologa; za proizvode je potrebna nova proizvodnja za uobičajene materijale, obično se isporučuju za 10-15 dana; za proizvode je potrebna nova proizvodnja za posebne i rijetke materijale, obično je potrebno 20-30 dana za isporuku.
2.P: Mogu li posjetiti vašu tvornicu?
O: Svakako, dobrodošli da posjetite našu tvornicu u bilo kojem trenutku.
3.P: Gdje si?
O: Anyang u provinciji Henan.
4.P: Koje certifikate imaju vaši proizvodi?
O: Imamo ISO 9001, BV, SGS, CE, TUV i druge certifikate.
5.P: Koji su vaši uvjeti plaćanja?
O: 30% T/T depozita unaprijed, 70% T/T salda u roku od 5 dana nakon B/L kopije, 100%. Neopozivi L/C po viđenju, 100% Neopozivi L/C nakon primitka B/L 30-120 dana, O/A.
Označiti:
Mn13, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel