NM450Tuf high-toughness crack-resistant and wear-resistant steel ensures that the wear resistance remains unchanged, while the impact energy at -20℃ can reach 110J.
The low-temperature toughness is more than twice that of the same level of wear-resistant steel and 4 times higher than the national standard requirements. It can serve in an environment of -60℃, and the wear resistance and service life are doubled without increasing the cost of processing technology such as welding.
- Giới thiệu chung
- Sản phẩm tương tự
- High Hardness and Excellent Wear Resistance:The surface hardness of NM450Tuf wear-resistant plate reaches 450HB. Hardness directly determines the wear resistance of the material. The higher the hardness, the stronger the wear resistance. Therefore, NM450Tuf wear-resistant plate can effectively cope with long-term wear and friction. In high-wear working conditions such as mining, crushing and transportation, it can greatly reduce the wear degree of equipment and reduce the replacement frequency, thereby improving production efficiency.
- Super Strong Impact Resistance:Through special smelting and treatment processes, NM450Tuf wear-resistant plate can still maintain high toughness under high impact loads to avoid cracks.
- Độ ổn định nhiệt tuyệt vời:NM450Tuf wear-resistant plate is not only suitable for high-temperature working environment, but also has excellent thermal stability. Many wear-resistant materials are prone to performance degradation or even brittle fracture when encountering sudden temperature changes, but NM450Tuf wear-resistant plate can effectively withstand temperature fluctuations and maintain stable working performance.
Sự miêu tả:
NM450Tuf wear-resistant plate is an ultra-high chống mài mòn steel plate, which belongs to low-alloy high-strength steel with a surface hardness of 450HB (Brinell hardness). It is developed based on the traditional wear-resistant plate NM450 steel plate, and adopts a series of special smelting processes to enhance its performance in high-wear and high-impact environments, especially in terms of impact resistance, toughness and thermal stability.
NM450Tuf wear-resistant plate is not only superior to general wear-resistant materials in hardness, but its high strength and impact resistance enable it to work normally in environments that many traditional wear-resistant steel plates cannot withstand, especially under strong impact and high load conditions, it is more stable.
NM450Tuf Specifications:
|
Loại thép |
Sức mạnh năng suất (MPa) |
Độ bền kéo (MPa) |
Độ giãn dài (A50%) |
Độ cứng Brinell (HBW) |
Năng lượng tác động (KV2, J) |
Thông số kỹ thuật có sẵn (mm) |
|
NM450Tuf |
≥1100 (1290) |
≥1300 (1540) |
≥7 (16.5) |
420-480 (453) |
≥48 (106) |
3.0-25.0 * 1000-2050 |
Main Characteristics of NM450Tuf Wear-resistant Plate:
Ứng dụng
NM450Tuf is widely used in mining, metallurgy, construction machinery, logistics and transportation, agricultural machinery and other fields.
Đóng gói sản phẩm:
Chúng tôi sử dụng những cách đóng gói an toàn nhất và hiệu quả nhất cho mọi loại hình giao hàng.
Hỏi đáp:
1.Q: Có thể giao hàng trong bao lâu?
Trả lời: Đối với các sản phẩm có sẵn, sẽ thực hiện giao hàng trong vòng 5 - 7 ngày sau khi nhận được tiền đặt cọc; đối với các sản phẩm cần sản xuất mới cho các nguyên liệu thông thường, thường thực hiện giao hàng trong 10 - 15 ngày; đối với các sản phẩm cần sản xuất mới cho các vật liệu đặc biệt và quý hiếm, thường cần 20-30 ngày để thực hiện lô hàng.
2.Q: Tôi có thể ghé thăm nhà máy của bạn không?
A: Chắc chắn, chào mừng bạn đến thăm nhà máy của chúng tôi bất cứ lúc nào.
3.Q: Bạn đang ở đâu?
A: Anyang ở tỉnh Hà Nam.
4.Q: Sản phẩm của bạn có những chứng nhận gì?
Trả lời: Chúng tôi có các chứng nhận ISO 9001, BV, SGS, CE, TUV và các chứng chỉ khác.
5.Q: Điều khoản thanh toán của bạn là gì?
A: đặt cọc trước 30% T/T, số dư 70% T/T trong vòng 5 ngày sau khi sao chép B/L, 100%. L/C không thể thu hồi ngay, L/C 100% không thể thu hồi sau khi nhận được B/L 30-120 ngày, O/A.
Nhãn:
NM450Tuf, China High Ductility Brittle Crack Arrest Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,Độ dẻo cao Giòn Crack Bắt giữ Thép chống mài mòn,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,NM400Tuf