X120Mn12 Manganese Plates
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Genel Bakış
- İlgili Ürünler
Açıklama:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
Bunlar steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Özellikler:
|
Ürün adı |
High Manganese steel plate |
|
Malzeme |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Marka |
TISCO, Bao Steel |
|
Standart |
DIN, GB, ISO, JIS, AISI, ASTM |
|
uzunluk |
2m için 7m |
|
genişlik |
1m için 2m |
|
Kalınlık |
3mm için 50mm |
Eşdeğer Notlar X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
Bir 128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25-0.50 |
≤0.100 |
≤0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
sınıf |
Gerilme direnci |
Akma dayanımı |
Uzama |
Shock Absorption (Water) |
Sertlik |
|
X120Mn12 |
880-1130 MPa |
≥410MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229HB |
Özellikler:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
Uygulamalar:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Ürün Ambalaj:
Her türlü teslimatınız için en güvenli ve en etkili paketleme yöntemlerini kullanıyoruz.
SSS:
1.Q: Teslimat ne kadar sürede yapılabilir?
C: Stoktaki ürünler için, depozito alındıktan sonra 5-7 gün içinde sevkiyat yapılacaktır; ürünler için ortak malzemeler için yeni üretime ihtiyaç duyulur, genellikle 10-15 gün içinde sevkiyat yapılır; Ürünler için özel ve nadir malzemeler için yeni üretime ihtiyaç duyulur, sevkiyatın yapılması genellikle 20-30 güne ihtiyaç duyar.
2.Q: Fabrikanızı ziyaret edebilir miyim?
C: Elbette, fabrikamızı istediğiniz zaman ziyaret etmenizi bekliyoruz.
3.S: Neredesin?
C: Henan Eyaletindeki Anyang.
4.Q: Ürünlerinizin hangi sertifikaları var?
C: ISO 9001, BV, SGS, CE, TUV ve diğer sertifikalarımız var.
5.Q: Ödeme koşullarınız nelerdir?
A:% 30 T/T depozitosu peşin, % 70 T/T bakiyesi konşimento kopyasından sonraki 5 gün içinde, % 100. Görüşte geri dönülemez akreditif, aldıktan sonra % 100 geri dönülemez akreditif B/L 30-120 günler, O/A.
Etiket:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 High Manganese Steel Plate