X120Mn12 Pllaka Mangani
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Përmbledhje
- Produkte te ndryshme
Përshkrim:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
këto steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
specifikimet:
|
Emri i produktit |
High Manganese steel plate |
|
material |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Markë |
TISCO, Bao Steel |
|
standard |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Gjatësi |
2m deri 7m |
|
Gjerësi |
1m deri 2m |
|
Trashësia |
3mm të 50mm |
Notat ekuivalente të X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
Një 128 |
10 BW |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤0.100 |
≤0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Klasë |
Forca elastik |
Fuqia e fitimit |
zgjatim |
Shock Absorption (Water) |
Fortësi |
|
X120Mn12 |
880 - 1130 MPa |
≥ 410 MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Karakteristika:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
Aplikimet:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Paketimi i produktit:
Ne përdorim mënyrat më të sigurta dhe më efektive të paketimit për të gjitha llojet e dërgesave.
FAQ:
1.P: Sa kohë mund të bëjë shpërndarjen?
A: Për produktet e aksioneve, do të bëjë dërgesat në 5- 7 ditë pas marrjes së depozitës; për produktet kanë nevojë për prodhim të ri për materiale të zakonshme, zakonisht dërgohen në 10-15 ditë; për produktet duhet prodhim i ri për materiale të veçanta dhe të rralla, zakonisht duhen 20-30 ditë për të kryer dërgesën.
2.P: A mund ta vizitoj fabrikën tuaj?
A: Sigurisht, ju mirëpresim të vizitoni fabrikën tonë në çdo kohë.
3.P: Ku jeni?
A: Anyang në provincën Henan.
4.P: Çfarë çertifikimesh kanë produktet tuaja?
Përgjigje: Ne kemi ISO 9001, BV, SGS, CE, TUV dhe certifikata të tjera.
5.P: Cilat janë kushtet tuaja të pagesës?
A: 30% depozitë T/T paraprakisht, 70% balanca T/T brenda 5 ditëve pas kopjes B/L, 100%. L/C e pakthyeshme në shikim, 100% L/C e pakthyeshme pas marrjes B/L 30-120 ditë, O/A.
tag:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 High Manganese Steel Plate