X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Visão geral
- Produtos relacionados
Descrição:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
Este steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Especificações:
|
Nome do Produto |
High Manganese steel plate |
|
Material |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Marcas |
TISCO, Bao Steel |
|
Standard |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Comprimento |
2m para 7m |
|
Largura |
1m para 2m |
|
Espessura |
3mm para 50mm |
Notas equivalentes de X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
A 128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Grade |
Resistência à Tração |
Resistência ao escoamento |
Alongamento |
Shock Absorption (Water) |
Dureza |
|
X120Mn12 |
880 - 1130 MPa |
≥ 410 MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Características:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
Aplicações:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Embalagem do produto:
Utilizamos as formas de embalagem mais seguras e eficazes para todos os tipos de entregas.
FAQ:
1.Q: Quanto tempo pode fazer a entrega?
R: Para produtos em estoque, faremos remessas em 5 a 7 dias após o recebimento do depósito; para produtos que necessitam de nova produção para materiais comuns, geralmente fazem envios em 10-15 dias; pois os produtos precisam de nova produção para materiais especiais e raros, geralmente precisam de 20 a 30 dias para fazer o envio.
2.Q:Posso visitar sua fábrica?
A: Claro, bem-vindo a visitar nossa fábrica a qualquer momento.
3.Q:Onde você está?
R: Anyang na província de Henan.
4.Q: Quais certificações seus produtos possuem?
R: Temos ISO 9001, BV, SGS, CE, TUV e outras certificações.
5.Q: Quais são as suas condições de pagamento?
A: depósito de 30% T/T adiantado, saldo de 70% T/T dentro de 5 dias após a cópia B/L, 100%. L/C irrevogável à vista, 100% L/C irrevogável após receber B/L 30-120 dias, O/A.
Tag:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 Placa de aço com alto teor de manganês