NM450Tuf high-toughness crack-resistant and wear-resistant steel ensures that the wear resistance remains unchanged, while the impact energy at -20℃ can reach 110J.
The low-temperature toughness is more than twice that of the same level of wear-resistant steel and 4 times higher than the national standard requirements. It can serve in an environment of -60℃, and the wear resistance and service life are doubled without increasing the cost of processing technology such as welding.
- Zakładka Podgląd
- Podobne produkty
- High Hardness and Excellent Wear Resistance:The surface hardness of NM450Tuf wear-resistant plate reaches 450HB. Hardness directly determines the wear resistance of the material. The higher the hardness, the stronger the wear resistance. Therefore, NM450Tuf wear-resistant plate can effectively cope with long-term wear and friction. In high-wear working conditions such as mining, crushing and transportation, it can greatly reduce the wear degree of equipment and reduce the replacement frequency, thereby improving production efficiency.
- Super Strong Impact Resistance:Through special smelting and treatment processes, NM450Tuf wear-resistant plate can still maintain high toughness under high impact loads to avoid cracks.
- Doskonała stabilność termiczna:NM450Tuf wear-resistant plate is not only suitable for high-temperature working environment, but also has excellent thermal stability. Many wear-resistant materials are prone to performance degradation or even brittle fracture when encountering sudden temperature changes, but NM450Tuf wear-resistant plate can effectively withstand temperature fluctuations and maintain stable working performance.
Opis:
NM450Tuf wear-resistant plate is an ultra-high odporne na zużycie steel plate, which belongs to low-alloy high-strength steel with a surface hardness of 450HB (Brinell hardness). It is developed based on the traditional wear-resistant plate NM450 steel plate, and adopts a series of special smelting processes to enhance its performance in high-wear and high-impact environments, especially in terms of impact resistance, toughness and thermal stability.
NM450Tuf wear-resistant plate is not only superior to general wear-resistant materials in hardness, but its high strength and impact resistance enable it to work normally in environments that many traditional wear-resistant steel plates cannot withstand, especially under strong impact and high load conditions, it is more stable.
NM450Tuf Specifications:
|
Gatunki stali |
Granica plastyczności (MPa) |
Wytrzymałość na rozciąganie (MPa) |
Wydłużenie (A50%) |
Twardość Brinella (HBW) |
Energia uderzenia (KV2, J) |
Dostępna specyfikacja (mm) |
|
NM450Tuf |
≥1100 (1290) |
≥1300 (1540) |
≥7 (16.5) |
420-480 (453) |
≥48 (106) |
3.0-25.0*1000-2050 |
Main Characteristics of NM450Tuf Wear-resistant Plate:
Aplikacje:
NM450Tuf is widely used in mining, metallurgy, construction machinery, logistics and transportation, agricultural machinery and other fields.
Opakowanie produktu:
Stosujemy najbezpieczniejsze i najskuteczniejsze metody pakowania dla wszystkich rodzajów przesyłek.
FAQ:
1. P: Jak długo można dokonać dostawy?
Odp.: w przypadku produktów magazynowych wysyłka nastąpi w ciągu 5–7 dni od otrzymania wpłaty; w przypadku produktów wymagających nowej produkcji dla typowych materiałów, przesyłki zwykle realizują w ciągu 10-15 dni; w przypadku produktów wymagających nowej produkcji specjalnych i rzadkich materiałów, zwykle potrzeba 20-30 dni na wysyłkę.
2. P: Czy mogę odwiedzić Twoją fabrykę?
Odp .: Oczywiście, zapraszamy do odwiedzenia naszej fabryki w dowolnym momencie.
3. P: Gdzie jesteś?
O: Anyang w prowincji Henan.
4. P: Jakie certyfikaty posiadają Twoje produkty?
Odp.: Posiadamy certyfikaty ISO 9001, BV, SGS, CE, TUV i inne.
5. P: Jakie są warunki płatności?
Odp.: 30% depozytu T/T z góry, 70% salda T/T w ciągu 5 dni po kopii B/L, 100%. Nieodwołalna akredytywa w zasięgu wzroku, 100% nieodwołalna akredytywa po otrzymaniu B/L 30-120 dni, O/A.
Tag:
NM450Tuf, China High Ductility Brittle Crack Arrest Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,Stal odporna na zużycie o wysokiej ciągliwości, zatrzymująca kruche pęknięcia,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,NM400Tuf