X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- סקירה כללית
- מוצרים קשורים
תיאור:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
אלה steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
פירוט מוצר:
|
שם מוצר |
High Manganese steel plate |
|
חוֹמֶר |
Din 1.3401, K700, Mn13, X120Mn12 |
|
מותג |
TISCO, Bao Steel |
|
תֶקֶן |
DIN, GB, ISO, JIS, AISI, ASTM |
|
אורך |
2m ל 7m |
|
רוֹחַב |
1m ל 2m |
|
עוֹבִי |
3mm ל50mm |
ציונים שוות ערך של X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
חַד |
|
1.3401 |
128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
ציון |
חוזק מתיחה |
כוח תשואה |
הַאֲרָכָה |
Shock Absorption (Water) |
קשיות |
|
X120Mn12 |
880 - 1130 MPa |
≥410MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
מאפיינים:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
יישומים:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
אריזת מוצר:
אנו משתמשים בדרכי האריזה הבטוחות והיעילות ביותר עבור כל סוגי המשלוחים.
שאלות ותשובות:
1. ש: כמה זמן יכול לבצע משלוח?
ת: עבור מוצרי מלאי, יבצע משלוחים תוך 5-7 ימים לאחר קבלת הפיקדון; עבור מוצרים צריכים ייצור חדש עבור חומרים נפוצים, בדרך כלל לבצע משלוחים תוך 10-15 ימים; עבור מוצרים צריך ייצור חדש עבור חומרים מיוחדים ונדירים, בדרך כלל צריך 20-30 ימים לבצע משלוח.
2. ש: האם אני יכול לבקר במפעל שלך?
ת: בטח, ברוך הבא לבקר במפעל שלנו בכל עת.
3. ש: איפה אתה?
ת: אניאנג במחוז הנאן.
4. ש: אילו אישורים יש למוצרים שלך?
ת: יש לנו ISO 9001, BV, SGS, CE, TUV ואישורים אחרים.
5. ש: מהם תנאי התשלום שלך?
ת: 30% הפקדת T/T מראש, יתרת T/T 70% בתוך 5 ימים לאחר העתקת B/L, 100%. L/C בלתי הפיך למראה, 100% L/C בלתי הפיך לאחר קבלת B/L 30-120 ימים, O/A.
תגים:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 High Manganese Steel Plate