Piastre al manganese X120Mn12
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Panoramica
- Spesso acquistati insieme
Descrizione:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
Alcuni degli steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Specifiche tecniche:
|
nome del prodotto |
High Manganese steel plate |
|
Materiali |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Brand |
TISCO, Bao Steel |
|
Standard |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Lunghezza |
2m a 7m |
|
Larghezza |
1m a 2m |
|
Spessore |
3mm a 50mm |
Gradi equivalenti di X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
A 128 |
BW 10 |
Z 120 M 12 |
X 120 Minuti 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25-0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Classe |
Resistenza alla trazione |
carico di snervamento |
Allungamento |
Shock Absorption (Water) |
Durezza |
|
X120Mn12 |
880 - 1130 MPa |
≥ 410 MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Caratteristiche:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
applicazioni:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Imballaggio del prodotto:
Utilizziamo i metodi di imballaggio più sicuri ed efficaci per tutti i tipi di consegne.
FAQ:
1.Q: Per quanto tempo è possibile effettuare la consegna?
R: Per i prodotti in stock, le spedizioni verranno effettuate entro 5-7 giorni dalla ricezione del deposito; per i prodotti che necessitano di nuova produzione per materiali comuni, solitamente si effettuano spedizioni in 10-15 giorni; per i prodotti che necessitano di nuova produzione per materiali speciali e rari, di solito sono necessari 20-30 giorni per effettuare la spedizione.
2.Q: Posso visitare la vostra fabbrica?
A: Certo, benvenuto a visitare la nostra fabbrica in qualsiasi momento.
3.Q:Dove sei?
R: Anyang nella provincia di Henan.
4.Q: Quali certificazioni hanno i vostri prodotti?
A: Abbiamo ISO 9001,BV, SGS, CE, TUV e altre certificazioni.
5.Q: Quali sono i termini di pagamento?
A: Deposito T/T del 30% in anticipo, saldo T/T del 70% entro 5 giorni dalla copia B/L, 100%. L/C irrevocabile a vista, L/C irrevocabile al 100% dopo aver ricevuto B/L 30-120 giorni, O/A.
Etichetta:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 High Manganese Steel Plate