Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match.
- Panoramica
- Spesso acquistati insieme
Descrizione:
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match. Under the action of large impact load or large contact stress, the surface of the steel plate is work hardened, and the surface hardness is rapidly increased from HB200 to above HB500, thereby producing a highly wear-resistant surface layer, while the inner austenite of the steel plate still maintains good impact toughness.
There are two characteristics of high manganese steel:
1.The greater the external impact load, the higher the wear resistance of its own surface layer;
2.As the surface hardened layer gradually wears away, a new work hardening layer will be continuously formed.
The special properties of high manganese steel are suitable for making wear-resistant components that withstand long-term wear of high impact materials. It has long been widely used in mechanical equipment such as metallurgy, mining, building materials, railways, electricity, and coal.
Specifiche tecniche:
|
Articolo |
MN13 |
|
Larghezza |
1000 fino a 3000 mm |
|
Grado standard |
BACCANO:1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 IT : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF: FORA500, FORA400,; Creusabro8000, Creusabro4800 GB: NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS: JFE-EH400, JFE-EH360, JFE-EH500; WEL-DURO500, WEL-DURO400 |
|
Processo tecnologico |
laminazione controllata, laminazione a caldo, normalizzazione, rinvenimento, ricottura, tempra, N+T, Q+T |
|
Spessore |
2 fino a 300 mm |
|
superficie |
pulizia, sabbiatura, finitura e verniciatura |
|
Lunghezza |
1000 fino a 12000 mm |
Equivalent Grades of Mn13:
|
GB |
EN |
ASTM |
AFNOR |
|
Mn13 |
1.3401-X120Mn13 |
A128GrB2 |
X120Mn13 |
Mn13 Chemical Composition:
|
Classe |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90 ~ 1.20 |
0.3 ~ 0.8 |
11.0 ~ 14.0 |
≤ 0.035 |
≤ 0.030 |
Mn13 Mechanical Property:
|
Classe |
Resistenza alla trazione (Mpa) |
Allungamento (%) |
Impact Performance(20℃) |
Initial Hardness Value (HB) |
Hardness Value After Hardening (HB) |
Cold Bending(180°) |
|
Mn13 |
≥ 800 |
≥ 40 |
ak≥90（J） |
200-250 |
> 300 |
Qualificato |
applicazioni:
Mn13 is often used to make shovel teeth of excavators, rolling wall and crushing wall of cone crushers, fork plates of jaw crushers, lining plates of ball mills, railway switches, plate hammers, hammer heads, etc.
Imballaggio del prodotto:
Utilizziamo i metodi di imballaggio più sicuri ed efficaci per tutti i tipi di consegne.
FAQ:
1.Q: Per quanto tempo è possibile effettuare la consegna?
R: Per i prodotti in stock, le spedizioni verranno effettuate entro 5-7 giorni dalla ricezione del deposito; per i prodotti che necessitano di nuova produzione per materiali comuni, solitamente si effettuano spedizioni in 10-15 giorni; per i prodotti che necessitano di nuova produzione per materiali speciali e rari, di solito sono necessari 20-30 giorni per effettuare la spedizione.
2.Q: Posso visitare la vostra fabbrica?
A: Certo, benvenuto a visitare la nostra fabbrica in qualsiasi momento.
3.Q:Dove sei?
R: Anyang nella provincia di Henan.
4.Q: Quali certificazioni hanno i vostri prodotti?
A: Abbiamo ISO 9001,BV, SGS, CE, TUV e altre certificazioni.
5.Q: Quali sono i termini di pagamento?
A: Deposito T/T del 30% in anticipo, saldo T/T del 70% entro 5 giorni dalla copia B/L, 100%. L/C irrevocabile a vista, L/C irrevocabile al 100% dopo aver ricevuto B/L 30-120 giorni, O/A.
Etichetta:
Mn13, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel