Plaques de manganèse X120Mn12
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Aperçu
- Produits annexes
Description:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
Ces steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Spécifications :
|
Nom du produit |
High Manganese steel plate |
|
Matières |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Marque |
TISCO, Bao Steel |
|
Standard |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Longueur |
2m à 7m |
|
Largeur |
1m à 2m |
|
Épaisseur |
3mm à 50mm |
Grades équivalents de X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
|
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Alliage |
Résistance à la traction |
Résistance au rendement |
Élongation |
Shock Absorption (Water) |
Dureté |
|
X120Mn12 |
880 à 1130 MPa |
410 MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Caractéristiques :
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
Applications :
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Emballage du produit:
Nous utilisons les moyens d’emballage les plus sûrs et les plus efficaces pour tous les types de livraisons.
FAQ:
1.Q : Combien de temps peut-on effectuer la livraison ?
R : Pour les produits en stock, les expéditions seront effectuées dans les 5 à 7 jours après réception du dépôt ; pour les produits qui nécessitent une nouvelle production pour des matériaux courants, les expéditions sont généralement effectuées en 10 à 15 jours ; Pour les produits nécessitant une nouvelle production pour des matériaux spéciaux et rares, il faut généralement 20 à 30 jours pour effectuer l'expédition.
2.Q: Puis-je visiter votre usine?
R: Bien sûr, bienvenue à vous visiter notre usine à tout moment.
3.Q : Où es-tu ?
R : Anyang, province du Henan.
4.Q : Quelles certifications vos produits ont-ils ?
R : Nous avons les certifications ISO 9001, BV, SGS, CE, TUV et autres.
5.Q: Quels sont vos conditions de paiement?
A : Dépôt de 30 % T/T à l'avance, solde de 70 % T/T dans les 5 jours après la copie B/L, 100 % L/C irrévocable à vue, 100 % L/C irrévocable après réception de B/L 30-120 jours, O/A.
Tag:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 Plaque d'acier à haute teneur en manganèse