Mn13 korkea mangaaniteräslevy
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match.
- Yleiskatsaus
- Liittyvät tuotteet
Kuvaus:
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match. Under the action of large impact load or large contact stress, the surface of the steel plate is work hardened, and the surface hardness is rapidly increased from HB200 to above HB500, thereby producing a highly wear-resistant surface layer, while the inner austenite of the steel plate still maintains good impact toughness.
There are two characteristics of high manganese steel:
1.The greater the external impact load, the higher the wear resistance of its own surface layer;
2.As the surface hardened layer gradually wears away, a new work hardening layer will be continuously formed.
The special properties of high manganese steel are suitable for making wear-resistant components that withstand long-term wear of high impact materials. It has long been widely used in mechanical equipment such as metallurgy, mining, building materials, railways, electricity, and coal.
Tekniset tiedot:
|
erä |
MN13 |
|
Leveys |
1000 - 3000 mm |
|
Vakioluokka |
DIN: 1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 FI : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF: FORA500, FORA400,; Creusabro8000, Creusabro4800 GB: NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS: JFE-EH400, JFE-EH360, JFE-EH500; WEL-HARD500, WEL-HARD400 |
|
Teknologinen prosessi |
ohjattu valssaus, kuumavalssattu, normalisointi, karkaisu, hehkutus, karkaisu, N+T, Q+T |
|
Paksuus |
2 - 300 mm |
|
pinta |
puhdistus, puhallus, viimeistely ja maalaus |
|
Pituus |
1000 - 12000 mm |
Equivalent Grades of Mn13:
|
GB |
EN |
ASTM |
AFNOR |
|
Mn13 |
1.3401-X120Mn13 |
A128GrB2 |
X120Mn13 |
Mn13 Chemical Composition:
|
Luokka |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90 ~ 1.20 |
0.3 ~ 0.8 |
11.0 ~ 14.0 |
≤ 0.035 |
≤ 0.030 |
Mn13 Mechanical Property:
|
Luokka |
Vetolujuus (MPa) |
Pidentymä (%) |
Impact Performance(20℃) |
Initial Hardness Value (HB) |
Hardness Value After Hardening (HB) |
Cold Bending(180°) |
|
Mn13 |
≥ 800 |
≥ 40 |
ak≥90（J） |
200-250 |
> 300 |
Hyväksytty |
Sovellukset:
Mn13 is often used to make shovel teeth of excavators, rolling wall and crushing wall of cone crushers, fork plates of jaw crushers, lining plates of ball mills, railway switches, plate hammers, hammer heads, etc.
Tuotepakkaus:
Käytämme turvallisimpia ja tehokkaimpia pakkaustapoja kaikentyyppisissä toimituksissa.
FAQ:
1.Q: Kuinka kauan voi toimittaa?
V: Varastotuotteille lähettää lähetykset 5-7 päivän kuluessa talletuksen vastaanottamisesta; tuotteille, jotka tarvitsevat uutta tuotantoa yleisille materiaaleille, toimitetaan yleensä 10-15 päivässä; tuotteille tarvitaan uutta tuotantoa erityisille ja harvinaisille materiaaleille, yleensä tarvitaan 20-30 päivää lähetyksen tekemiseen.
2.K: Voinko vierailla tehtaallasi?
V: Toki, tervetuloa käymään tehtaallamme milloin tahansa.
3.K: Missä olet?
V: Anyang Henanin maakunnassa.
4.K: Mitä sertifikaatteja tuotteillasi on?
V: Meillä on ISO 9001, BV, SGS, CE, TUV ja muut sertifikaatit.
5.K: Mitkä ovat maksuehtosi?
A: 30 % T/T-talletus etukäteen, 70 % T/T-saldo 5 päivän sisällä B/L-kopion jälkeen, 100 % Peruuttamaton L/C nähdessäsi, 100 % peruuttamaton L/C vastaanotettuasi B/L 30-120 päivää, O/A.
Tag:
Mn13, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel