X120Mn12 Manganese Plates
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- بررسی اجمالی
- محصولات مرتبط
شرح:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
اینها steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
مشخصات:
|
نام محصول |
High Manganese steel plate |
|
ماده |
Din 1.3401, K700, Mn13, X120Mn12 |
|
نام تجاری |
TISCO, Bao Steel |
|
استاندارد |
DIN, GB, ISO, JIS, AISI, ASTM |
|
طول |
2m به 7m |
|
عرض |
1m به 2m |
|
ضخامت |
3mm به 50mm |
نمرات معادل از X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
128 |
10 BW |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
درجه |
استحکام کششی |
نیروی تولید |
کشیدگی |
Shock Absorption (Water) |
سختی |
|
X120Mn12 |
880 - 1130 مگاپاسکال |
≥ 410 مگاپاسکال |
≥ 40٪ |
124 J (at room temperature) |
≤ 229 HB |
امکانات:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
برنامه های کاربردی:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
بسته بندی محصول:
ما از ایمن ترین و موثرترین روش های بسته بندی برای انواع تحویل استفاده می کنیم.
پرسش و پاسخ:
1.Q: چه مدت می تواند تحویل را انجام دهد؟
A: برای محصولات سهام، 5-7 روز پس از دریافت سپرده، حمل و نقل را انجام می دهد. برای محصولات نیاز به تولید جدید برای مواد معمولی دارند، معمولاً در 10-15 روز حمل و نقل می کنند. برای محصولات نیاز به تولید جدید برای مواد خاص و کمیاب دارد، معمولاً 20-30 روز برای حمل و نقل نیاز دارد.
2.Q: آیا می توانم از کارخانه شما بازدید کنم؟
پاسخ: مطمئناً ، در هر زمان به کارخانه ما خوش آمدید.
3. س: کجا هستید؟
ج: آنیانگ در استان هنان.
4.Q: محصولات شما چه گواهینامه هایی دارند؟
A: ما گواهینامه های ISO 9001، BV، SGS، CE، TUV و سایر موارد را داریم.
5.Q: شرایط پرداخت شما چیست؟
A: 30% سپرده T/T پیش پرداخت، 70% موجودی T/T ظرف 5 روز پس از کپی B/L، 100%. روز، O/A.
برچسب:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 High Manganese Steel Plate