Mn13 High Manganese Steel Plate
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match.
- Ülevaade
- Seotud tooted
Kirjeldus:
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match. Under the action of large impact load or large contact stress, the surface of the steel plate is work hardened, and the surface hardness is rapidly increased from HB200 to above HB500, thereby producing a highly wear-resistant surface layer, while the inner austenite of the steel plate still maintains good impact toughness.
There are two characteristics of high manganese steel:
1.The greater the external impact load, the higher the wear resistance of its own surface layer;
2.As the surface hardened layer gradually wears away, a new work hardening layer will be continuously formed.
The special properties of high manganese steel are suitable for making wear-resistant components that withstand long-term wear of high impact materials. It has long been widely used in mechanical equipment such as metallurgy, mining, building materials, railways, electricity, and coal.
Tehnilised andmed:
|
Kirje |
MN13 |
|
LAIUS |
1000 kuni 3000 mm |
|
Standardne hinne |
DIN: 1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 ET : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF: FORA500, FORA400,; Creusabro8000, Creusabro4800 GB: NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS : JFE-EH400, JFE-EH360, JFE-EH500; WEL-HARD500, WEL-HARD400 |
|
Tehnoloogiline protsess |
kontrollitud valtsimine, kuumvaltsitud, normaliseerimine, karastamine, lõõmutamine, karastamine, N+T, Q+T |
|
LOHVI PAKSUS |
2 kuni 300 mm |
|
Pind |
puhastamine, lõhkamine, viimistlemine ja värvimine |
|
Pikkus |
1000 kuni 12000 mm |
Equivalent Grades of Mn13:
|
GB |
EN |
ASTM |
AFNOR |
|
Mn13 |
1.3401-X120Mn13 |
A128GrB2 |
X120Mn13 |
Mn13 Chemical Composition:
|
Klass |
C |
Si |
Mn |
P |
S |
|
Mn13 |
0.90 ~ 1.20 |
0.3 ~ 0.8 |
11.0 ~ 14.0 |
≤ 0.035 |
≤ 0.030 |
Mn13 Mechanical Property:
|
Klass |
Tõmbetugevus (MPa) |
Pikendus (%) |
Impact Performance(20℃) |
Initial Hardness Value (HB) |
Hardness Value After Hardening (HB) |
Cold Bending(180°) |
|
Mn13 |
≥800 |
≥40 |
ak≥90（J） |
200-250 |
> 300 |
Kvalifitseeritud |
Rakendused:
Mn13 is often used to make shovel teeth of excavators, rolling wall and crushing wall of cone crushers, fork plates of jaw crushers, lining plates of ball mills, railway switches, plate hammers, hammer heads, etc.
Toote pakkimine:
Kasutame igat liiki tarnete puhul kõige ohutumaid ja tõhusamaid pakkimisviise.
FAQ:
1.Q: Kui kaua saab tarnida?
V: Laotoodete puhul saadab saadetised 5–7 päeva jooksul pärast tagatisraha saamist; toodete puhul, mis vajavad tavaliste materjalide jaoks uut tootmist, teostage saadetised tavaliselt 10-15 päevaga; toodete jaoks on vaja uut tootmist spetsiaalsete ja haruldaste materjalide jaoks, tavaliselt kulub saatmiseks 20-30 päeva.
2.Q: Kas ma saan teie tehast külastada?
V: Muidugi, tere tulemast külastama meie tehast igal ajal.
3.K: Kus sa oled?
V: Anyang Henani provintsis.
4.Q: Millised sertifikaadid teie toodetel on?
V: Meil on ISO 9001, BV, SGS, CE, TUV ja muud sertifikaadid.
5.Q: Millised on teie maksetingimused?
A: 30% T/T sissemakse ette, 70% T/T saldo 5 päeva jooksul pärast B/L koopiat, 100%.Tühistamatu L/C nägemisel, 100% tühistamatu L/C pärast B/L 30-120 saamist päeva, O/A.
tag:
Mn13, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel