X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Επισκόπηση
- Σχετικά προϊόντα
Περιγραφή:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
Αυτοί steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Προδιαγραφές:
|
όνομα προϊόντος |
High Manganese steel plate |
|
Υλικα |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Μάρκα |
TISCO, Bao Steel |
|
Βασική |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Μήκος |
2m να 7m |
|
Πλάτος |
1m να 2m |
|
Πάχος |
3mm να 50mm |
Ισοδύναμοι Βαθμοί των X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
Μια 128 |
10 BW |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Βαθμός |
Αντοχή σε εφελκυσμό |
Αντοχή απόδοσης |
επιμήκυνση |
Shock Absorption (Water) |
Σκληρότητα |
|
X120Mn12 |
880 - 1130 MPa |
≥ 410 MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Χαρακτηριστικά:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
εφαρμογές:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Συσκευασία προϊόντος:
Χρησιμοποιούμε τους πιο ασφαλείς και αποτελεσματικούς τρόπους συσκευασίας για όλους τους τύπους παραδόσεων.
FAQ:
1.Q: Πόσο καιρό μπορεί να κάνει την παράδοση;
Α: Για προϊόντα στοκ, θα πραγματοποιήσει αποστολές σε 5-7 ημέρες μετά την παραλαβή της κατάθεσης. για τα προϊόντα χρειάζονται νέα παραγωγή για κοινά υλικά, συνήθως πραγματοποιούν αποστολές σε 10-15 ημέρες. για τα προϊόντα χρειάζονται νέα παραγωγή για ειδικά και σπάνια υλικά, χρειάζονται συνήθως 20-30 ημέρες για να γίνει η αποστολή.
2.Q: Μπορώ να επισκεφτώ το εργοστάσιό σας;
Α: Σίγουρα, καλώς ήρθατε να επισκεφτείτε το εργοστάσιό μας ανά πάσα στιγμή.
3. Ε: Πού είσαι;
Α: Anyang στην επαρχία Henan.
4.Q: Τι πιστοποιήσεις έχουν τα προϊόντα σας;
Α: Έχουμε ISO 9001, BV, SGS, CE, TUV και άλλες πιστοποιήσεις.
5.Q: Ποιοι είναι οι όροι πληρωμής σας;
A: 30% κατάθεση T/T εκ των προτέρων, 70% υπόλοιπο T/T εντός 5 ημερών μετά την αντιγραφή B/L, 100%. Ανέκκλητο L/C σε όψη, 100% Ανέκκλητο L/C μετά τη λήψη B/L 30-120 ημέρες, O/A.
Ετικέτα:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Μn13 High Manganese Steel Plate