X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Karta Přehled
- Související produkty
Popis:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
Tyto steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Specifikace:
|
jméno výrobku |
High Manganese steel plate |
|
Materiál |
Din 1.3401, K700, Mn13, X120Mn12 |
|
značka |
TISCO, Bao Steel |
|
Standard |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Délka |
2 až 7 metrů |
|
Šířka |
1 až 2 metrů |
|
Tloušťka |
3mm na 50mm |
Ekvivalentní známky X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25-0.50 |
≤0.100 |
≤0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Stupeň |
Pevnost v tahu |
Síla výtěžnosti |
Prodloužení |
Shock Absorption (Water) |
Tvrdost |
|
X120Mn12 |
880 - 1130 MPa |
≥ 410 MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Funkce:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
Aplikace:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Balení produktu:
Pro všechny typy dodávek používáme nejbezpečnější a nejefektivnější způsoby balení.
FAQ:
1.Q: Jak dlouho může být dodávka?
Odpověď: U skladových produktů bude zásilka odeslána do 5-7 dnů po obdržení zálohy; pro produkty potřebují novou výrobu pro běžné materiály, obvykle expedice do 10-15 dnů; pro produkty potřebují novou výrobu pro speciální a vzácné materiály, obvykle potřebují 20-30 dní na odeslání.
2.Q: Mohu navštívit vaši továrnu?
Odpověď: Jistě, můžete kdykoli navštívit naši továrnu.
3.Q: Kde jsi?
A: Anyang v provincii Henan.
4.Q: Jaké certifikace mají vaše produkty?
Odpověď: Máme certifikace ISO 9001, BV, SGS, CE, TUV a další.
5.Q: Jaké jsou vaše platební podmínky?
A: 30% záloha T/T předem, 70% T/T zůstatek do 5 dnů po B/L kopii, 100%.Neodvolatelný akreditiv na viděnou, 100% neodvolatelný akreditiv po obdržení B/L 30-120 dny, O/A.
Štítek:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn 13 High Manganese Steel Plate