Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match.
- Karta Přehled
- Související produkty
Popis:
Mn13 is the choice of wear-resistant materials that can resist strong impact, high pressure material wear, etc. It has work hardening characteristics that other wear-resistant materials cannot match. Under the action of large impact load or large contact stress, the surface of the steel plate is work hardened, and the surface hardness is rapidly increased from HB200 to above HB500, thereby producing a highly wear-resistant surface layer, while the inner austenite of the steel plate still maintains good impact toughness.
There are two characteristics of high manganese steel:
1.The greater the external impact load, the higher the wear resistance of its own surface layer;
2.As the surface hardened layer gradually wears away, a new work hardening layer will be continuously formed.
The special properties of high manganese steel are suitable for making wear-resistant components that withstand long-term wear of high impact materials. It has long been widely used in mechanical equipment such as metallurgy, mining, building materials, railways, electricity, and coal.
Specifikace:
|
Položka |
MN13 |
|
Šířka |
1000 až 3000 mm |
|
Standardní známka |
DIN: 1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 EN : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF : FORA500, FORA400,; Creusabro8000, Creusabro4800 GB: NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS: JFE-EH400, JFE-EH360, JFE-EH500; WEL-HARD500, WEL-HARD400 |
|
Technologický proces |
řízené válcování, válcování za tepla, normalizace, popouštění, žíhání, kalení, N+T, Q+T |
|
Tloušťka |
2 až 300 mm |
|
povrch |
čištění, tryskání, konečná úprava a lakování |
|
Délka |
1000 až 12000 mm |
Equivalent Grades of Mn13:
|
GB |
EN |
ASTM |
AFNOR |
|
Mn 13 |
1.3401-X120Mn13 |
A128GrB2 |
X120Mn13 |
Mn13 Chemical Composition:
|
Stupeň |
C |
Si |
Mn |
P |
S |
|
Mn 13 |
0.90 1.20 ~ |
0.3 0.8 ~ |
11.0 14.0 ~ |
≤0.035 |
≤0.030 |
Mn13 Mechanical Property:
|
Stupeň |
Pevnost v tahu (MPa) |
Prodloužení (%) |
Impact Performance(20℃) |
Initial Hardness Value (HB) |
Hardness Value After Hardening (HB) |
Cold Bending(180°) |
|
Mn 13 |
≥800 |
≥40 |
ak≥90（J） |
200-250 |
> 300 |
Kvalifikovaný |
Aplikace:
Mn13 is often used to make shovel teeth of excavators, rolling wall and crushing wall of cone crushers, fork plates of jaw crushers, lining plates of ball mills, railway switches, plate hammers, hammer heads, etc.
Balení produktu:
Pro všechny typy dodávek používáme nejbezpečnější a nejefektivnější způsoby balení.
FAQ:
1.Q: Jak dlouho může být dodávka?
Odpověď: U skladových produktů bude zásilka odeslána do 5-7 dnů po obdržení zálohy; pro produkty potřebují novou výrobu pro běžné materiály, obvykle expedice do 10-15 dnů; pro produkty potřebují novou výrobu pro speciální a vzácné materiály, obvykle potřebují 20-30 dní na odeslání.
2.Q: Mohu navštívit vaši továrnu?
Odpověď: Jistě, můžete kdykoli navštívit naši továrnu.
3.Q: Kde jsi?
A: Anyang v provincii Henan.
4.Q: Jaké certifikace mají vaše produkty?
Odpověď: Máme certifikace ISO 9001, BV, SGS, CE, TUV a další.
5.Q: Jaké jsou vaše platební podmínky?
A: 30% záloha T/T předem, 70% T/T zůstatek do 5 dnů po B/L kopii, 100%.Neodvolatelný akreditiv na viděnou, 100% neodvolatelný akreditiv po obdržení B/L 30-120 dny, O/A.
Štítek:
Mn13, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel