X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- Overview
- Свързани продукти
Описание:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
тези steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
Спецификации:
|
Име на продукта |
High Manganese steel plate |
|
Материал |
Din 1.3401, K700, Mn13, X120Mn12 |
|
Бранд |
TISCO, Bao Steel |
|
Standard |
DIN, GB, ISO, JIS, AISI, ASTM |
|
Дължина |
2м до 7м |
|
Ширина |
1м до 2м |
|
Дебелина |
3mm да 50mm |
Еквивалентни степени на X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
А 128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25 - 0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
Клас |
Издръжливост на опън |
Провлачване |
удължаване |
Shock Absorption (Water) |
Твърдост |
|
X120Mn12 |
880 - 1130 МРа |
≥410MPa |
≥ 40% |
124 J (at room temperature) |
≤ 229 HB |
Характеристики:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
Приложения:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
Опаковка на продукта:
Използваме най-безопасните и ефективни начини за опаковане за всички видове доставки.
Често задавани въпроси:
1.Q: Колко време може да направи доставката?
A: За складови продукти ще направи пратки в рамките на 5-7 дни след получаване на депозита; за продукти се нуждаят от ново производство за общи материали, обикновено правят пратки за 10-15 дни; за продукти се нуждаят от ново производство за специални и редки материали, обикновено се нуждаят от 20-30 дни, за да направят пратката.
2.Q: Мога ли да посетя вашата фабрика?
A: Разбира се, добре дошли да посетите нашата фабрика по всяко време.
3.Q: Къде си?
О: Анянг в провинция Хенан.
4.Q: Какви сертификати имат вашите продукти?
О: Имаме ISO 9001, BV, SGS, CE, TUV и други сертификати.
5.Q: Какви са вашите условия на плащане?
A: 30% T/T депозит предварително, 70% T/T баланс в рамките на 5 дни след B/L копие, 100%. Неотменим L/C при виждане, 100% Неотменим L/C след получаване на B/L 30-120 дни, O/A.
Tag:
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 High Manganese Steel Plate