X120Mn12 Manganese Plates
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability.
- نظرة عامة
- المنتجات ذات الصلة
الوصف:
X120Mn12 manganese steel plate (also called manganese hard steel or hard manganese steel plate) has the characteristics of significantly increasing the original low hardness and tensile strength of the cold-worked layer in the quenched state, which is achieved by intensive cold working, but without adversely affecting the original very high durability. Cold working greatly improves the wear resistance of X120MN12 steel plate. X120MN12 grade manganese steel plate can be flanged, bent and perforated due to its high durability.
X120Mn12 steel is a high manganese steel plate with an austenitic structure, which is characterized by a high manganese content (about 12%) and a high carbon content (average 1.00-1.20%). The concentration range of manganese and carbon depends on the equivalent of different source grades.
تشبه steel plates are classified according to material, standard grade, thickness, width and length, and are made into two different forms - sheets and plates.
مواصفات:
|
اسم المنتج |
High Manganese steel plate |
|
الخامة |
Din 1.3401, K700, Mn13, X120Mn12 |
|
العلامات التجارية |
TISCO, Bao Steel |
|
المجموعة الأساسية |
DIN, GB, ISO, JIS, AISI, ASTM |
|
الطول |
2m إلى 7m |
|
عرض |
1m إلى 2m |
|
سماكة |
3mm ل50mm |
الدرجات المعادلة X120Mn12:
|
DIN |
AISI |
BS |
AFNOR |
UNI |
|
1.3401 |
و128 |
BW 10 |
Z 120 M 12 |
X 120 Mn 12 |
X120Mn12 Manganese Steel Plate Chemical Composition:
|
C |
Mn |
Si |
P |
S |
Cr |
|
1.10 - 1.30 |
11.00 - 14.00 |
0.25-0.50 |
≤ 0.100 |
≤ 0.040 |
1.50 |
X120Mn12 Mechanical Properties at Room Temperature:
|
الصف |
قوة الشد |
قوة الغلة |
استطالة |
Shock Absorption (Water) |
عسر الماء |
|
X120Mn12 |
880 - 1130 ميجا باسكال |
≥ 410 ميجا باسكال |
≥ 40٪ |
124 J (at room temperature) |
≤ 229 هب |
المميزات:
Surface hardening during grinding and crushing, good ductility, impact resistance and the ability to withstand dynamic loads are basic criteria for selecting and using steel.
High manganese steel is non-magnetic steel after proper heat treatment.
High hardness of the material in the supersaturated state - about 500 HBW.
التطبيقات:
X120Mn12 high manganese steel plates are widely used in industrial and general purposes, such as crusher jaws, electric shovel bolts, impact mills, centrifugal mills, protective grilles, doors, crusher jaw inserts, electric shovel connectors, clamping teeth, cladding and safety plates.
التعبئة المنتج:
نحن نستخدم أكثر طرق التغليف أمانًا وفعالية لجميع أنواع التسليمات.
أسئلة وأجوبة:
1. س: كم من الوقت يمكن إجراء التسليم؟
ج: بالنسبة لمنتجات المخزون، سيتم إجراء الشحنات خلال 5 - 7 أيام بعد استلام الودائع؛ بالنسبة للمنتجات التي تحتاج إلى إنتاج جديد للمواد الشائعة، عادة ما يتم الشحن خلال 10-15 يومًا؛ بالنسبة للمنتجات التي تحتاج إلى إنتاج جديد للمواد الخاصة والنادرة، عادةً ما تحتاج إلى 20-30 يومًا لإجراء الشحن.
2. س: يمكنني زيارة المصنع الخاص بك؟
ج: بالتأكيد ، أرحب بكم بزيارة مصنعنا في أي وقت.
3.س: أين أنت؟
ج: أنيانغ في مقاطعة خنان.
4. س: ما هي الشهادات التي تمتلكها منتجاتك؟
ج: لدينا شهادات ISO 9001 وBV وSGS وCE وTUV وغيرها.
5 موك: ما هي شروط الدفع الخاصة بك؟
ج: إيداع 30% T/T مقدمًا، و70% رصيد T/T في غضون 5 أيام بعد نسخة B/L، 100%. خطاب اعتماد غير قابل للإلغاء في الأفق، 100% خطاب اعتماد غير قابل للإلغاء بعد استلام B/L 30-120 أيام، يا/أ.
افضل
X120Mn12 Manganese Plates, China High Mn Wear-Resistant Steel Manufacturers, Suppliers, Factory, Wear-Corrosion-Resistant Steel,High-Class Hardened And Tempered Wear-Resistant Steel,High Ductility Brittle Crack Arrest Wear-Resistant Steel,Super Wear-Resistant Steel,High-Temperature And Wear Resistant Steel,High Mn Wear-Resistant Steel,Low Yield Ratio Wear-Resistant Steel,Mn13 صفيحة فولاذية عالية المنغنيز